1.5mm Bright / Soap-coated 302 Stainless Steel Spring Wire for Heavy-duty Applications

Matt 200 / 300 /400 series Stainless Steel Spring Wire

Construction Stainless Steel Spring Wire 302 Stainless Steel Wire JIS G4314 Standard

General Properties

302 is a variations of the 18% chromium / 8% nickel austenitic alloy, which is the most familiar and the most frequently used in the stainless steel family. Alloy 302 is a slightly higher carbon version of 304, often found in strip and wire forms. It is a tough, ductile grade that demonstrates comparable corrosion resistance, is non-magnetic, and is not hardenable by heat treatment. Alloy 302 is usually used in its annealed condition and has a high ease of fabrication and formability.

Chemical Properties:

Mechanical Properties:

Physical Properties:

Corrosion Resistance

1, Provides useful resistance to corrosion on a wide range of moderately oxidizing to moderately reducing environments

2, The 18 -19% of chromium which this alloy contains provides resistance to oxidizing environments such as dilute nitric acid.

3, Resistant to moderately aggressive organic acids such as acetic, and reducing acids such as phosphoric.

4,’The 9-11% of nickel contained in this alloy provides resistance to moderately reducing environments.

Machinability

Slow speeds and high feeds will overcome this alloy’s tendency to work-harden

Due to gummy chips, it is recommended that chip breakers are used on all tooling

Weldability

Can best be welded by resistance or shielded fusion methods

Post weld annealing dissolves the chromium carbide and is recommended for maximum resistance to intergranular attack

Hot Working

Uniform heating to 2100oF will allow this allow to be forged, upset and headed successfully

Do not work below 1700oF

Cold Working

Will dramatically increase the hardness of this material; however, it is quite ductile and may readily be drawn, spun and upset

Causes alloy 302 to become magnetic

Post-fabrication annealing is necessary to retain maximum corrosion resistance and a non-magnetic condition